High speed measurement is realized by adopting high temperature superconductivity magnet.
Hmax = 6Tesla, Ful l Loop measurement becomes possible in 2minutes.
(This company’s existing machine: Full Loop measurement needs 40 minutes.)
[VSM-5HSC] High Temperature Superconducting Type of Vibrating Sample Magnetometer
The world’ s first* of one-twentieth of measurement speed is realized compared to this company’ s existing product by adopting high temperature superconductivity magnet to VSM.
Br, HcJ high accuracy measurement of 0.5 mm cube magnet becomes possible.
Possible FORC&SORC measurement.
*Investigated as of July, 2014 by Toei Industry Co., Ltd.
![[VSM-5HSC] High Temperature Superconducting Type of Vibrating Sample Magnetometer](../../images/products/sei-01/pt_vsm-5hsc_s.jpg)
Click to enlarge images.
Features
Realization of High Speed Measurement
High Accuracy Measurement of Small Sample of Br, HcJ
High accuracy measurement of Br, HcJ of 0.5 mm cube magnet, intensity distribution etc. of Br, HcJ and comparative measurement of micro-changed amount by cutting out surface reforming area become possible.
Also, comparative measurement of finishing degradation becomes possible.
FORC&SORC Measurement
Evaluation of interaction between particles and coercive force distribution (particle diameter) becomes possible.
Sample Temperature Variable Measurement
-50℃ - +200℃ temperature variable UNIT(Option)
Miniaturization of Magnetic Field Generation part
Size of magnet system part: 0.8 x 0.3 x 0.3 m